    • IR Thermography of Steel Specimens undergoing Tensile Tests 

      Stange, Even; Khawaja, Hassan (Conference object, 2018-12-13)
      In this work, the IR thermography was used to study the steel specimens (DIN 50125 Standard) undergoing the tensile tests. The tensile tests were performed using GUNT® Hamburg Universal Material Tester. The tensile specimens were clamped, and the test force was generated using a hand-operated hydraulic system. A dial gauge measured the elongation of the specimens. Using the WP 300.20 system for data ...

    • Multiphysics Study of Tensile Testing using Infrared thermography 

      Stange, Even; Andleeb, Zahra; Khawaja, Hassan; Moatamedi, Mojtaba (Journal article; Peer reviewed, 2019)
      In this work, the IR thermography was used to study the steel specimens (DIN 50125 Standard) undergoing the tensile tests. The tensile tests were performed using GUNT® Hamburg Universal Material Tester. The tensile specimens were clamped, and the test force was generated using a handoperated hydraulic system. A dial gauge measured the elongation of the specimens. Using the WP 300.20 system for data ...

    • Qualitative visualization of the development of stresses through infrared thermography 

      Stange, Even; Andleeb, Zahra; Khawaja, Hassan (Journal article; Peer reviewed, 2019)
      In this work, the IR thermography was used to study the steel specimens (DIN 50125 Standard) undergoing the tensile tests. The tensile tests were performed using GUNT® Hamburg Universal Material Tester. The tensile specimens were clamped, and the test force was applied using a hand-operated hydraulic system. A dial gauge measured the elongation of the specimens. Using the WP 300.20 system for data ...

    • Thermography and tensile tests of steel samples. Study of material properties and internal friction effects 

      Stange, Even (Master thesis; Mastergradsoppgave, 2018-06-01)
      The thesis presents analysis of material properties and internal effects in steel samples, with varying temperatures. Uniaxial tensile tests were conducted in both room temperature and low temperatures, to generate graphical measures of the mechanical properties. The steel samples were monitored with thermography throughout the course of the tensile tests, to investigate the heat generation associated ...